Effect of different concentrations of specific inhibitor of matrix metalloproteinases on the shear bond strength of self-adhesive resin cements to de…
2017
Background Considering the probability of chemical and enzymatic reactions between matrix metalloproteinases (MMPs) in the dentin structure and their specific inhibitors, the aim of the present study was to evaluate the effect of different concentrations of specific inhibitor of MMPs (galardin) on the shear bond strength of self-adhesive resin cements to dentin. Material and Methods Forty-eight sound human premolars were mounted in self-cured acrylic resin after removal of the enamel on the buccal and lingual surfaces. The dentin surfaces achieved were polished and prepared with 600-grit silicon carbide paper. The samples were divided into 3 groups (n=16) based on the concentration of galar…
Applications of confocal laser scanning microscopy to dental bonding.
1998
The introduction of confocal laser scanning microscopy (CLSM) has provided a valuable new technique for the visualization of bonding structures such as a hybrid layer in dentin (Watson, 1989, 1991), In the case of seven commercially-available dentin bonding systems, it could be demonstrated that the CLSM renders considerably more detailed information than the SEM because of its nondestructive nature and because of the possibility of a distinction between components of bonding agents. With most of the bonding systems, measurements of the thickness of the hybrid layer could be carried out when the primer component was labeled with rhodamine B. It was found that this thickness is significantl…
Hybrid layers of etch-and-rinse versus self-etching adhesive systems.
2010
Objective: To evaluate the effectiveness in the formation of resin tags, adhesive lateral branches and hybrid layers of five adhesive systems, when bonding to dentine. Material and Methods: Flat dentin surfaces from 25 molars were bonded with several adhesive systems according to the manufacturers? instructions. Composite build-ups were constructed incrementally with Tetric Ceram. The Specimens were sectioned parallel to the long axis. One section was treated with phosphoric acid and sodium hypochlorite in order to reveal the hybrid layer formation. The other section was stored in 30% hydrochloric acid to detect resin tags and adhesive lateral branch formation. Results: The two etch-and-rin…
Current dental adhesives systems. A narrative review.
2012
Adhesive dentistry is based on the development of materials which establish an effective bond with the tooth tissues. In this context, adhesive systems have attracted considerable research interest in recent years. Successful adhesive bonding depends on the chemistry of the adhesive, on appropriate clinical handling of the material as well as on the knowledge of the morphological changes caused on dental tissue by different bonding procedures. This paper outlines the status of contemporary adhesive systems, with particular emphasis on chemical characteristics and mode of interaction of the adhesives with enamel and dentinal tissues. Dental adhesives are used for several clinical application…
Effect of self-etching primer/adhesive and conventional bonding on the shear bond strength in metallic and ceramic brackets
2011
Introduction: Bracket debonding from the tooth surface is a common problem in fixed orthodontics. The aims of the present study were to assess the bond strength and failure sites in two ways of bonding technique, with metallic and ceramic brackets. Material and Methods: One hundred premolars were assigned to 4 groups of 25 each: Group A, metallic brackets/ conventional procedure; Group B, metallic brackets/Transbond XT; Group C, ceramic brackets/conventional procedure; and Group D, ceramic brackets/Transbond XT. Transbond XT composite paste was used for bracket bonding and cured by conventional light-cure device. Specimens were subjected to thermocycling. One week after bonding shearing for…
How can droplet formation occur in endodontically treated teeth during bonding procedures?
2008
PURPOSE: The aim of this in vivo study was to clarify how blistering formation occurs along intraradicular dentin bonded interfaces. MATERIALS AND METHODS: Patients were selected and post space was prepared in vivo in endodontically treated teeth. Post space was etched, dried with ethanol, and bonded with one of the following adhesive systems: All Bond 2, XP-Bond, Clearfil SE Bond, Xeno III. The four adhesives were considered as representative of each bonding system class. An additional group was prepared with phosphoric acid treatment + application of Pre-Bond unfilled resin of All Bond 2, without the use of the primer agent. Etching was avoided for self-etching materials. Replicas of the …
Bond strength of selected composite resin-cements to zirconium-oxide ceramic
2012
Objectives: The aim of this study was to evaluate bond strengths of zirconium-oxide (zirconia) ceramic and a selection of different composite resin cements. Study Design: 130 Lava TM cylinders were fabricated. The cylinders were sandblasted with 80 μm aluminium oxide or silica coated with CoJet Sand. Silane, and bonding agent and/or Clearfil Ceramic Primer were applied. One hundred thirty composite cement cylinders, comprising two dual-polymerizing (Variolink II and Panavia F) and two autopolymerizing (Rely X and Multilink) resins were bonded to the ceramic samples. A shear test was conducted, followed by an optical microscopy study to identify the location and type of failure, an elec…
In vitro experimental study of bonding between aluminium oxide ceramics and resin cements
2010
To evaluate bond strengths of different resin cements to two aluminum oxide-based ceramics. Methods: One hundred ten ceramic cylinders were produced and given four different surface treatments. Resin cement cylinders were then bonded to the ceramic cylinders using different resin cements and the bond strength was determined by shear testing to the breaking point. We were thus able to obtain results for the different combinations of porcelain, surface treatments and cements. All data was analyzed using the Kruskal-Wallis test for more than two independent samples and the Bonferroni correction applied (a=0.01). An optical microscopy study was carried out to analyze the type of failure, and an…
Resistance to bond degradation between dual-cure resin cements and pre-treated sintered CAD-CAM dental ceramics
2012
Objective: To evaluate the bond stability of resin cements when luted to glass-reinforced alumina and zirconia CAD/CAM dental ceramics. Study design: Eighteen glass-infiltrated alumina and eighteen densely sintered zirconia blocks were randomly conditioned as follows: Group 1: No treatment; Group 2: Sandblasting (125 µm Al2O3-particles); and Group 3: Silica-coating (50 µm silica-modified Al2O3-particles). Composite samples were randomly bonded to the pre-treated ceramic surfaces using different resin cements: Subgroup 1: Clearfil Esthetic Cement (CEC); Subgroup 2: RelyX Unicem (RXU); and Subgroup 3: Calibra (CAL). After 24 h, bonded specimens were cut into 1 ± 0.1 mm2 sticks. One-half of th…
Bond strength evaluation of the veneering-core ceramics bonds.
2009
The purpose of this study was to determine whether the bond of veneering porcelain to a ceramic core in bilayered ceramics was similar to that of the metal ceramic control of well known behaviour. Six groups of nine specimens each were fabricated, whose dimensions were 15 mm long and 8 mm in diameter at the core, and 2 mm long and 8 mm in diameter for the veneer. The groups were GR. 1 (control group): CrNi alloy/d.SIGN (Ivoclar), GR. 2: IPS e.maxPress/IPS e.maxCeram (Ivoclar), GR. 3: IPS e.maxZirCad/ IPS e.maxZirPress (Ivoclar), GR. 4: IPS e.maxZirCad/IPS e.maxCeram (Ivoclar), GR. 5: Lava Frame (3M ESPE)/ Lava Ceram (3M ESPE) and GR. 6: Lava Frame (3M ESPE)/IPS e.maxCeram (Ivoclar). A shear…